Hemorrhages are still considered a common cause of death and despite the availability of different hemostatic agents it is still necessary to develop more effective hemostats for bleeding managements in emergency situations. Herein, large-pores mesoporous silica microspheres (MSM) were synthesized, and their surface was modified to enrich the hydroxyls population with the aim of achieving a material with enhanced water adsorption capacity and high hemostatic ability. The success of surface modification was investigated by Fourier Transform Infrared spectroscopy (FT-IR) and thermogravimetric analysis (TGA), which confirmed the increase in the amount of surface hydroxyl groups. A hemolysis assay as well as a clotting test were carried out to evaluate the hemocompatibility and hemostatic ability, respectively. It was found that the modified material presented the lowest hemolytic ratio and the lowest clotting time. The novelty of the paper is mainly due to the coupling of the hemostatic ability test with the adsorption microcalorimetry of water. In fact, being the water adsorption on the material surface a crucial factor in the hemostatic activity, microcalorimetry was used for the first time to study the adsorption of water and estimate its heat of adsorption. The data obtained showed that the modified MSM presents a surface able to adsorb a higher amount of water, compared to the pristine MSM, with a low molar heat of adsorption (about 35 kJ/mol), which renders the modified MSM presented in the present study an excellent candidate for producing novel hemostats.

New insights in large-pores mesoporous silica microspheres for hemostatic application / Mohamed, Sara Saber Younes; Cavalli, Roberta; Rombi, Elisabetta; Atzori, Luciano; Armandi, Marco; Onida, Barbara. - In: JOURNAL OF MATERIALS SCIENCE. MATERIALS IN MEDICINE. - ISSN 1573-4838. - ELETTRONICO. - 36:1(2025), pp. 1-9. [10.1007/s10856-025-06864-9]

New insights in large-pores mesoporous silica microspheres for hemostatic application

Mohamed, Sara Saber Younes;Armandi, Marco;Onida, Barbara
2025

Abstract

Hemorrhages are still considered a common cause of death and despite the availability of different hemostatic agents it is still necessary to develop more effective hemostats for bleeding managements in emergency situations. Herein, large-pores mesoporous silica microspheres (MSM) were synthesized, and their surface was modified to enrich the hydroxyls population with the aim of achieving a material with enhanced water adsorption capacity and high hemostatic ability. The success of surface modification was investigated by Fourier Transform Infrared spectroscopy (FT-IR) and thermogravimetric analysis (TGA), which confirmed the increase in the amount of surface hydroxyl groups. A hemolysis assay as well as a clotting test were carried out to evaluate the hemocompatibility and hemostatic ability, respectively. It was found that the modified material presented the lowest hemolytic ratio and the lowest clotting time. The novelty of the paper is mainly due to the coupling of the hemostatic ability test with the adsorption microcalorimetry of water. In fact, being the water adsorption on the material surface a crucial factor in the hemostatic activity, microcalorimetry was used for the first time to study the adsorption of water and estimate its heat of adsorption. The data obtained showed that the modified MSM presents a surface able to adsorb a higher amount of water, compared to the pristine MSM, with a low molar heat of adsorption (about 35 kJ/mol), which renders the modified MSM presented in the present study an excellent candidate for producing novel hemostats.
File in questo prodotto:
File Dimensione Formato  
s10856-025-06864-9.pdf

accesso aperto

Descrizione: New insights in large-pores mesoporous silica microspheres for hemostatic application
Tipologia: 2a Post-print versione editoriale / Version of Record
Licenza: Creative commons
Dimensione 1.22 MB
Formato Adobe PDF
1.22 MB Adobe PDF Visualizza/Apri
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11583/2997459