Inconel 625 (IN625) superalloys can be easily fabricated by the laser-based powder bed fusion (PBF-LB/M) process, allowing the production of components with a high level of design freedom. However, one of the main drawbacks of the PBF-LB/M process is the control over thermally induced stresses and their mitigation. A standard approach to prevent distortion caused by residual stress is performing a stress-relieving (SR) heat treatment before cutting the parts from the building platform. Differently from the cast or wrought alloy, in additively manufactured IN625, the standard SR at 870 °C provokes the early formation of the undesirable δ phase. Therefore, this unsuitable precipitation observed in the PBF-LB/M material drives the attention to develop a tailored SR treatment to minimise the presence of undesirable phases. This work investigates SR at lower temperatures by simultaneously considering their effects on residual stress mitigation, microstructural evolution, and mechanical properties. A multiscale approach with cantilever and X-ray technologies was used to investigate how the residual stress level is affected by SR temperature. Moreover, microstructural analyses and phase identifications were performed by SEM, XRD, EBSD, and DSC analyses. Finally, mechanical investigations through microhardness and tensile tests were performed as well. The results revealed that for the additively manufactured IN625 parts, an alternative SR treatment able to mitigate the residual stresses without a massive formation of δ phase could be performed in a temperature range between 750 and 800 °C.

Effects of Stress-Relieving Temperature on Residual Stresses, Microstructure and Mechanical Behaviour of Inconel 625 Processed by PBF-LB/M / Martucci, Alessandra; Marchese, Giulio; Bassini, Emilio; Lombardi, Mariangela. - In: METALS. - ISSN 2075-4701. - ELETTRONICO. - 13:4(2023). [10.3390/met13040796]

Effects of Stress-Relieving Temperature on Residual Stresses, Microstructure and Mechanical Behaviour of Inconel 625 Processed by PBF-LB/M

Alessandra Martucci;Giulio Marchese;Emilio Bassini;Mariangela Lombardi
2023

Abstract

Inconel 625 (IN625) superalloys can be easily fabricated by the laser-based powder bed fusion (PBF-LB/M) process, allowing the production of components with a high level of design freedom. However, one of the main drawbacks of the PBF-LB/M process is the control over thermally induced stresses and their mitigation. A standard approach to prevent distortion caused by residual stress is performing a stress-relieving (SR) heat treatment before cutting the parts from the building platform. Differently from the cast or wrought alloy, in additively manufactured IN625, the standard SR at 870 °C provokes the early formation of the undesirable δ phase. Therefore, this unsuitable precipitation observed in the PBF-LB/M material drives the attention to develop a tailored SR treatment to minimise the presence of undesirable phases. This work investigates SR at lower temperatures by simultaneously considering their effects on residual stress mitigation, microstructural evolution, and mechanical properties. A multiscale approach with cantilever and X-ray technologies was used to investigate how the residual stress level is affected by SR temperature. Moreover, microstructural analyses and phase identifications were performed by SEM, XRD, EBSD, and DSC analyses. Finally, mechanical investigations through microhardness and tensile tests were performed as well. The results revealed that for the additively manufactured IN625 parts, an alternative SR treatment able to mitigate the residual stresses without a massive formation of δ phase could be performed in a temperature range between 750 and 800 °C.
2023
File in questo prodotto:
File Dimensione Formato  
metals-13-00796+(5)_compressed.pdf

accesso aperto

Tipologia: 2a Post-print versione editoriale / Version of Record
Licenza: Creative commons
Dimensione 515.67 kB
Formato Adobe PDF
515.67 kB Adobe PDF Visualizza/Apri
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11583/2979740