IRIS è la soluzione IT che facilita la raccolta e la gestione dei dati relativi alle attività e ai prodotti della ricerca. Fornisce a ricercatori, amministratori e valutatori gli strumenti per monitorare i risultati della ricerca, aumentarne la visibilità e allocare in modo efficace le risorse disponibili.
EnglishA key aspect of ceramic matrix composites integration is related to a reliable joining technique. An ytterbium disilicate based glass-ceramic material is processed by reactive viscous flow sintering between a barium aluminium borosilicate glass and ytterbium oxide and it is used to join SiC/SiC and C/SiC composites. The joining temperature and the in situ formation of the Yb2Si2O7 is optimised at 1200°C without pressure, on the basis of the sintering and crystallisation mechanisms. The mechanical characterization of SiC/SiC and C/SiC joined with the ytterbium disilicate-based glass-ceramic, tested by single-lap offset at RT, exhibits an apparent shear strength of 35 MPa, similar to their interlaminar shear strength. The proposed system displays self-healing behaviour at 1000 °C and 1150 °C, as demonstrated by the partial and complete sealing of induced cracks by Vickers indentation on its surface at different loads, thus suggesting that it can effectively be used as promising joining material for CMCs.
Ytterbium disilicate-based glass-ceramic as joining material for ceramic matrix composites / Smeacetto, F.; D'Isanto, F.; Casalegno, V.; Tatarko, P.; Salvo, M.. - In: JOURNAL OF THE EUROPEAN CERAMIC SOCIETY. - ISSN 0955-2219. - 41:2(2021), pp. 1099-1106. [10.1016/j.jeurceramsoc.2020.10.022]
| Titolo: | Ytterbium disilicate-based glass-ceramic as joining material for ceramic matrix composites | |
| Autori: | ||
| Data di pubblicazione: | 2021 | |
| Rivista: | ||
| Digital Object Identifier (DOI): | http://dx.doi.org/10.1016/j.jeurceramsoc.2020.10.022 | |
| Appare nelle tipologie: | 1.1 Articolo in rivista |
File in questo prodotto:
| File | Descrizione | Tipologia | Licenza | |
|---|---|---|---|---|
| 1-s2.0-S0955221920308359-main.pdf | post print editoriale | 2a Post-print versione editoriale / Version of Record | Non Pubblico - Accesso privato/ristretto | Administrator Richiedi una copia |
| manuscipt.pdf | pre-print pre-referaggio | 1. Preprint / Submitted Version | PUBBLICO - Tutti i diritti riservati | Visibile a tuttiVisualizza/Apri |
http://hdl.handle.net/11583/2856754
Copyright © 2022