IRIS è la soluzione IT che facilita la raccolta e la gestione dei dati relativi alle attività e ai prodotti della ricerca. Fornisce a ricercatori, amministratori e valutatori gli strumenti per monitorare i risultati della ricerca, aumentarne la visibilità e allocare in modo efficace le risorse disponibili.
EnglishSiC foams sandwiched between two Ceramic Matrix Composite (CMC) skins are of interest for several high temperature applications ranging from aeronautics to energy production. In this paper, SiC foams were joined to C/SiC composites by the “Mo-wrap” method to obtain sandwich structures. The Mo-wrap method is a recently developed joining technique: it consists of wrapping Si foils inside a Mo wrap in order to prevent molten silicon leaking from the joined area and infiltrating SiC foam and C/SiC during the joining process. Compression and thermal shock resistance tests were performed on the C/SiC – SiC foam – C/SiC sandwich obtaining sound results.
| Titolo: | SiC foam sandwich structures obtained by Mo-wrap joining |
| Autori: | |
| Data di pubblicazione: | 2018 |
| Rivista: | |
| Digital Object Identifier (DOI): | 10.1016/j.matlet.2018.03.105 |
| Appare nelle tipologie: | 1.1 Articolo in rivista |
File in questo prodotto:
| File | Descrizione | Tipologia | Licenza | |
|---|---|---|---|---|
| 1-s2.0-S0167577X18304695-main.pdf | 2a. Post-print Versione editoriale | Non Pubblico - Accesso privato/ristretto | Administrator Richiedi una copia | |
| SiC foam Mo wrap_ Mat letters 2018.pdf | 2. Post-print |  | Embargo: 20/03/2020 Richiedi una copia |
http://hdl.handle.net/11583/2705433
Copyright © 2019