In this article expandable graphitewas used to produce fire retardant biobased poly- lactide. For this purpose,PLAblends with addition of 1, 5 or 10 wt.%of expandable graphite inter- calated with sulphuric acid (GR) were obtained using co-rotating twin screw extruder. Thermal stability and flammability of prepared samples were examined by thermogravimetric analysis (TGA), cone calorimeter measurements and UL94 test. Flammability UL-94 test shows the highest V-0 ranking from 5 % graphite loading, whereas 10 % is required for sensible decrease of rate of combustion in cone calorimeter forced combustion test.
Flame retardant and thermal behavior of polylactide / expandable graphite composites / Wei, Ping; Bocchini, Sergio; Camino, Giovanni. - In: POLIMERY. - ISSN 0032-2725. - STAMPA. - 58:5(2013), pp. 361-364.
Flame retardant and thermal behavior of polylactide / expandable graphite composites
WEI, PING;BOCCHINI, SERGIO;CAMINO, GIOVANNI
2013
Abstract
In this article expandable graphitewas used to produce fire retardant biobased poly- lactide. For this purpose,PLAblends with addition of 1, 5 or 10 wt.%of expandable graphite inter- calated with sulphuric acid (GR) were obtained using co-rotating twin screw extruder. Thermal stability and flammability of prepared samples were examined by thermogravimetric analysis (TGA), cone calorimeter measurements and UL94 test. Flammability UL-94 test shows the highest V-0 ranking from 5 % graphite loading, whereas 10 % is required for sensible decrease of rate of combustion in cone calorimeter forced combustion test.Pubblicazioni consigliate
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.
https://hdl.handle.net/11583/2508899
Attenzione
Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo