Micronic ZSM5 (Si/Al = 25) powder has been deposited on cordierite monoliths by dip-coating technique using colloidal alumina or silica as binders with different zeolite/binder ratios in aqueous suspension determining the parameters to obtain the best adhesion and mechanical resistance of the washcoat layer. For monolithic catalysts with washcoat containing 10 wt% SiO2 the following alternative preparation procedures have been used: (i) deposition of a pre-exchanged Cu-ZSM5 powder on the ceramic monolith; (ii) deposition of a H-ZSM5 powder on the ceramic monolith followed by copper exchange of the structured catalyst. The monolithic catalysts have been investigated by morphological (SEM), physical (BET and porosity), chemical (ICP-MS, EDX, XRD, H2 TPR) and catalytic (NO decomposition tests in flow reactor under dry and wet conditions) analyses. Results have been compared with those obtained on the corresponding Cu-ZSM5 powder sample with the same copper content and Si/Al ratio in order to define the effect of the preparation procedure on the chemical and catalytic properties of the monoliths

Cu-ZSM-5 based monolith reactors for NO decomposition / Lisi, L.; Pirone, Raffaele; Russo, G.; Stanzione, V.. - In: CHEMICAL ENGINEERING JOURNAL. - ISSN 1385-8947. - STAMPA. - 154:1-3(2009), pp. 341-347. [10.1016/j.cej.2009.04.025]

Cu-ZSM-5 based monolith reactors for NO decomposition

PIRONE, RAFFAELE;
2009

Abstract

Micronic ZSM5 (Si/Al = 25) powder has been deposited on cordierite monoliths by dip-coating technique using colloidal alumina or silica as binders with different zeolite/binder ratios in aqueous suspension determining the parameters to obtain the best adhesion and mechanical resistance of the washcoat layer. For monolithic catalysts with washcoat containing 10 wt% SiO2 the following alternative preparation procedures have been used: (i) deposition of a pre-exchanged Cu-ZSM5 powder on the ceramic monolith; (ii) deposition of a H-ZSM5 powder on the ceramic monolith followed by copper exchange of the structured catalyst. The monolithic catalysts have been investigated by morphological (SEM), physical (BET and porosity), chemical (ICP-MS, EDX, XRD, H2 TPR) and catalytic (NO decomposition tests in flow reactor under dry and wet conditions) analyses. Results have been compared with those obtained on the corresponding Cu-ZSM5 powder sample with the same copper content and Si/Al ratio in order to define the effect of the preparation procedure on the chemical and catalytic properties of the monoliths
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11583/2496676
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo