The wear behaviour on prealloyed sintered steel parts TiCN PVD coating was analysed. Cylindrical specimens (phi 40x30 mm(3)) were compacted to the green density of similar to 7.0 g.cm(-3). The specimens were sintered in pusher furnace at the temperature of 1180 degrees C for 40 minutes in an atmosphere of 25H(2)+75N(2). Part of sintered specimens was then coated by Physical Vapour Deposition. Wear tests were carried out by means of a pin-on-disk tribometer. The results of profilograms (the values of surface roughness) and the wear curves (mass loss versus sliding distance) showed positive effect of coating on the wear resistance of the tested specimens.

Wear of TiCN coated sintered Fe-1.5Cr-0.2Mo-0.7C steels / R., Bidulsky; ACTIS GRANDE, Marco. - STAMPA. - 409:(2009), pp. 390-393. (Intervento presentato al convegno 3rd International conference on fractography of advanced ceramics tenutosi a Stara Lesna, Slovakia nel September 07-10, 2008) [10.4028/www.scientific.net/KEM.409.390].

Wear of TiCN coated sintered Fe-1.5Cr-0.2Mo-0.7C steels

ACTIS GRANDE, MARCO
2009

Abstract

The wear behaviour on prealloyed sintered steel parts TiCN PVD coating was analysed. Cylindrical specimens (phi 40x30 mm(3)) were compacted to the green density of similar to 7.0 g.cm(-3). The specimens were sintered in pusher furnace at the temperature of 1180 degrees C for 40 minutes in an atmosphere of 25H(2)+75N(2). Part of sintered specimens was then coated by Physical Vapour Deposition. Wear tests were carried out by means of a pin-on-disk tribometer. The results of profilograms (the values of surface roughness) and the wear curves (mass loss versus sliding distance) showed positive effect of coating on the wear resistance of the tested specimens.
2009
KEY ENGINEERING MATERIALS
4.1 Contributo in Atti di convegno
File in questo prodotto:
File Dimensione Formato  
43853_UPLOAD.pdf

accesso riservato

Tipologia: 2a Post-print versione editoriale / Version of Record
Licenza: Non Pubblico - Accesso privato/ristretto
Dimensione 1.77 MB
Formato Adobe PDF
  Visualizza/Apri   Richiedi una copia
1.77 MB Adobe PDF   Visualizza/Apri   Richiedi una copia
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11583/1856957
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo