Fourier transform IR spectroscopy of CO and N2, adsorbed at liquid nitrogen temperature, was used to characterize an MFI-type H-FeZSM-5 ferrisilicate which was synthesized with a Si/Fe ratio of 50. Thermal treatment of this material at 773 and 973 K was performed in order to follow formation of extraframework species. On samples fired at 773 K Brønsted acid sites were present which gave an O-H stretching band at 3630 cm–1. These hydroxyl groups formed adducts with both probe molecules, which were monitored by the corresponding bathochromic shift, . Corresponding values for adsorbed CO and N2 were = –270 and = – 100, respectively. Increasing the firing temperature up to 973 K led to complete removal of iron from the zeolite framework, and consequent disappearance of Brønsted acidity. In this process, extraframework iron oxide species were formed which were also characterized by IR spectroscopy of the adsorbed probe molecules. Both CO and N2 gave Lewis-type adducts with coordinatively unsaturated Fe3+ ions present in the extraframework material. A comparison is made with results of a previous study on the H-GaZSM-5 isomorph.

Infrared studies of the interaction of carbon monoxide and dinitrogen with ferrisilicate MFI-type zeolites / Zecchina, A; Geobaldo, Francesco; Lamberti, C; Bordiga, S; TURNES PALOMINO, G; OTERO AREAN, C.. - In: CATALYSIS LETTERS. - ISSN 1011-372X. - 42:1-2(1996), pp. 25-33. [10.1007/BF00814463]

Infrared studies of the interaction of carbon monoxide and dinitrogen with ferrisilicate MFI-type zeolites

GEOBALDO, FRANCESCO;
1996

Abstract

Fourier transform IR spectroscopy of CO and N2, adsorbed at liquid nitrogen temperature, was used to characterize an MFI-type H-FeZSM-5 ferrisilicate which was synthesized with a Si/Fe ratio of 50. Thermal treatment of this material at 773 and 973 K was performed in order to follow formation of extraframework species. On samples fired at 773 K Brønsted acid sites were present which gave an O-H stretching band at 3630 cm–1. These hydroxyl groups formed adducts with both probe molecules, which were monitored by the corresponding bathochromic shift, . Corresponding values for adsorbed CO and N2 were = –270 and = – 100, respectively. Increasing the firing temperature up to 973 K led to complete removal of iron from the zeolite framework, and consequent disappearance of Brønsted acidity. In this process, extraframework iron oxide species were formed which were also characterized by IR spectroscopy of the adsorbed probe molecules. Both CO and N2 gave Lewis-type adducts with coordinatively unsaturated Fe3+ ions present in the extraframework material. A comparison is made with results of a previous study on the H-GaZSM-5 isomorph.
1996
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11583/1640968
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo