Tellurium-Doped Silanised Bioactive Glass–Chitosan Hydrogels: A Dual Action for Antimicrobial and Osteoconductive Platforms

UV-cured methacrylated chitosan (MCHIT) hydrogels were achieved in the presence of silanised tellurium-doped silica bioactive glass (BG-Te-Sil) to produce an antimicrobial and osteoconductive scaffold for tissue engineering applications. Methacrylation of chitosan enabled efficient crosslinking, and the curing process was evaluated by means of Fourier-transform infrared spectroscopy (FTIR) and photorheology analyses. Compressive testing on crosslinked hydrogels showed that the silanised, bioactive, doped glass increased the hydrogel’s elastic modulus by up to 200% compared to unreinforced controls. Antibacterial assays against Staphylococcus aureus ATCC 43300 revealed a significant (p < 0.05) reduction in bacterial metabolic activity for hydrogels containing 50 wt% of the Te-doped bioactive glass. In vitro cytocompatibility with human bone-marrow mesenchymal stem cells demonstrated sustained viability and uniform distribution at 72 h (live/dead staining, AlamarBlue). Under H2O2-induced oxidative stress, reinforced hydrogels downregulated pro-inflammatory genes (TNF-α, IFN-γ, IL-1β, and PGES-2). These results suggest that the presence of the silanised bioactive glass can significantly enhance mechanical stability, antibacterial properties, and anti-inflammatory responses without affecting cytocompatibility, making these hydrogels promising for tissue engineering applications.