Be ITER-like wall at the JET tokamak under plasma

The JET tokamak is operated with beryllium and tungsten plasma-facing components to prepare for the exploitation of ITER. To determine beryllium erosion and migration in JET a set of markers were installed. Specimens from different beryllium marker tiles of the main wall of the ITER-like wall (ILW) JET tokamak from the first and the second D-D campaign were analyzed with nuclear reaction analysis, x-ray fluorescence spectroscopy, scanning electron microscopy and x-ray diffraction (XRD). Emphasis was on the determination of carbon plasma impurities deposited on beryllium surfaces. The C-12(d, p(0))C-13 reaction was used to quantify carbon deposition and to determine depth profiles. Carbon quantities on the surface of the Be tiles are low, varying from (0.35 +/- 0.07) x 10(17) to (11.8 +/- 0.6) x 10(17) at cm(-2) in the deposition depth from 0.4 to 6.7 mu m, respectively. In the 0.4-0.5 mm wide grooves of castellation sides the carbon content is found up to (14.3 +/- 2.5) x 10(17) at cm(-2) while it is higher (up to (38 +/- 4) x 10(17) at cm(-2)) in wider gaps (0.8 mm) separating tile segments. Oxygen (O), titanium (Ti), chromium (Cr), manganese (Mn), iron (Fe), nickel (Ni) and tungsten (W) were detected in all samples exposed to plasma and the reference one but at lower quantities at the latter. In the central part of the Inner Wall Guard Limiter from the first ILW campaign and in the Outer Poloidal Limiter from the second ILW campaign the Ni interlayer has been completely eroded. XRD shows the formation of BeNi in most specimens.