In this work, two types of CP Ti cubes with similar volumetric energy densities (VED) but different process parameters were produced using laser powder bed fusion (LPBF) method. The corrosion behavior of the fabricated specimens was investigated by conducting electrochemical impedance spectroscopy (EIS) and polarization experiments in simulated body fluid (SBF) solution at 37 °C. The results indicated that the microstructure and porosities, which are of great importance for biomedical applications, can be controlled by changing the process parameters even under constant energy densities. The sample produced with a lower laser power (E1) was featured with a higher level of porosity and thinner alpha laths, as compared with the sample fabricated with a higher laser power (E2). Moreover, results obtained from the bioactivity tests revealed that the sample produced with a higher laser power conferred a slight improvement in the bioactivity due to the higher amount of porosity. Lower laser power and hence higher porosity level promoted the formation of bone-like apatite on the surface of the printed specimens. The potentiodynamic polarization tests revealed inferior corrosion resistance for the fabricated sample with higher porosity. Moreover, the EIS results after different immersion times indicated that a stable oxide film was formed on the surface of samples for all immersion times. After 1 and 3 days of immersion, superior passivation behavior was observed for the sample fabricated with lower laser power. However, very similar impedance and phase values were observed for all the samples after 14 days of immersion.
Microstructure and Corrosion Properties of CP-Ti Processed by Laser Powder Bed Fusion under Similar Energy Densities / Mosallanejad, M. H.; Sanaei, S.; Atapour, M.; Niroumand, B.; Iuliano, L.; Saboori, A.. - In: ACTA METALLURGICA SINICA. - ISSN 1006-7191. - ELETTRONICO. - (2022). [10.1007/s40195-022-01376-9]
Microstructure and Corrosion Properties of CP-Ti Processed by Laser Powder Bed Fusion under Similar Energy Densities
Iuliano L.;Saboori A.
2022
Abstract
In this work, two types of CP Ti cubes with similar volumetric energy densities (VED) but different process parameters were produced using laser powder bed fusion (LPBF) method. The corrosion behavior of the fabricated specimens was investigated by conducting electrochemical impedance spectroscopy (EIS) and polarization experiments in simulated body fluid (SBF) solution at 37 °C. The results indicated that the microstructure and porosities, which are of great importance for biomedical applications, can be controlled by changing the process parameters even under constant energy densities. The sample produced with a lower laser power (E1) was featured with a higher level of porosity and thinner alpha laths, as compared with the sample fabricated with a higher laser power (E2). Moreover, results obtained from the bioactivity tests revealed that the sample produced with a higher laser power conferred a slight improvement in the bioactivity due to the higher amount of porosity. Lower laser power and hence higher porosity level promoted the formation of bone-like apatite on the surface of the printed specimens. The potentiodynamic polarization tests revealed inferior corrosion resistance for the fabricated sample with higher porosity. Moreover, the EIS results after different immersion times indicated that a stable oxide film was formed on the surface of samples for all immersion times. After 1 and 3 days of immersion, superior passivation behavior was observed for the sample fabricated with lower laser power. However, very similar impedance and phase values were observed for all the samples after 14 days of immersion.File | Dimensione | Formato | |
---|---|---|---|
Mosallanejad2022_Article_MicrostructureAndCorrosionProp.pdf
non disponibili
Tipologia:
2a Post-print versione editoriale / Version of Record
Licenza:
Non Pubblico - Accesso privato/ristretto
Dimensione
5.84 MB
Formato
Adobe PDF
|
5.84 MB | Adobe PDF | Visualizza/Apri Richiedi una copia |
Pubblicazioni consigliate
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.
https://hdl.handle.net/11583/2959288