In the context of the development of carriers for amino acids delivery, Spherical Mesoporous Silica Particles (SMSP), characterized by particles size ranging from 0.15 µm to 0.80 µm and average pore diameter of 2.4 nm, were synthesised and loaded with L-arginine (ARG), a basic amino acid involved in several physiological processes. The loading was performed using water as a solvent through the wet impregnation method (with a final arginine content of 9.1% w/w). The material was characterized before and after impregnation by means of X-Ray Diffraction (XRD), nitrogen sorption analysis, Field Emission Scanning Electron Microscopy (FESEM) and Fourier Transform Infrared (FT-IR) spectroscopy. SMSP are shown to suffer degradation upon impregnation, which dramatically affects their porosity. To elucidate the role of the pH of the ARG impregnating solution (originally set at pH ≈ 11) on SMSP degradation, the loading was performed under different pH conditions (5 and 9) keeping constant the ARG concentration. The impregnation performed with acidic solution did not modify the carrier. All samples displayed ARG in amorphous form: zwitterionic species were present in SMSP impregnated at basic pH whereas positive protonated species in that impregnated at acidic pH.

The role of the pH in the impregnation of spherical mesoporous silica particles with L-arginine aqueous solutions / Mohamed, SARA SABER YOUNES; Martinez, Sonia; Banchero, Mauro; Manna, Luigi; Ronchetti, SILVIA MARIA; Onida, Barbara. - In: INTERNATIONAL JOURNAL OF MOLECULAR SCIENCES. - ISSN 1422-0067. - ELETTRONICO. - 22:24(2021). [10.3390/ijms222413403]

The role of the pH in the impregnation of spherical mesoporous silica particles with L-arginine aqueous solutions

SARA SABER YOUNES MOHAMED;Mauro Banchero;Luigi Manna;Silvia Maria Ronchetti;Barbara Onida
2021

Abstract

In the context of the development of carriers for amino acids delivery, Spherical Mesoporous Silica Particles (SMSP), characterized by particles size ranging from 0.15 µm to 0.80 µm and average pore diameter of 2.4 nm, were synthesised and loaded with L-arginine (ARG), a basic amino acid involved in several physiological processes. The loading was performed using water as a solvent through the wet impregnation method (with a final arginine content of 9.1% w/w). The material was characterized before and after impregnation by means of X-Ray Diffraction (XRD), nitrogen sorption analysis, Field Emission Scanning Electron Microscopy (FESEM) and Fourier Transform Infrared (FT-IR) spectroscopy. SMSP are shown to suffer degradation upon impregnation, which dramatically affects their porosity. To elucidate the role of the pH of the ARG impregnating solution (originally set at pH ≈ 11) on SMSP degradation, the loading was performed under different pH conditions (5 and 9) keeping constant the ARG concentration. The impregnation performed with acidic solution did not modify the carrier. All samples displayed ARG in amorphous form: zwitterionic species were present in SMSP impregnated at basic pH whereas positive protonated species in that impregnated at acidic pH.
File in questo prodotto:
File Dimensione Formato  
ijms-22-13403.pdf

accesso aperto

Tipologia: 2a Post-print versione editoriale / Version of Record
Licenza: Creative commons
Dimensione 3.18 MB
Formato Adobe PDF
3.18 MB Adobe PDF Visualizza/Apri
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11583/2947393