Although addition of montmorillonite (MMT) clay to isotactic polypropylene (iPP) results in large increases in the melt viscosity at low shear rates, satisfactory impregnation of glass mats is obtained with iPP/MMT under conditions typical of industrial processing, and the MMT is well dispersed throughout the resulting composites. However, the MMT is also shown to retard relaxation of the glass mat, leading to non-uniform through-thickness glass fiber distributions. Thus, depending on the initial lay-up and hence on the initial surface fiber concentration, the bending modulus of the consolidated specimens may either increase or decrease with increasing matrix MMT content, whereas the tensile modulus remains consistent with the predictions of micromechanical models based on the assumption of a uniform glass fiber distribution. The presence of matrix-rich layers at surfaces of specimens containing MMT is also shown to promote crack initiation and induce premature failure in flexural tests.

Hybrid glass mat reinforced polypropylene-montmorillonite nanocomposites / Plummer, Christopher J. G.; Dalle Vacche, Sara; Houphouët-Boigny, Chrystèle; Michaud, Véronique; Månson, Jan-Anders E.. - In: DIFFUSION AND DEFECT DATA, SOLID STATE DATA. PART B, SOLID STATE PHENOMENA. - ISSN 1012-0394. - STAMPA. - 151:(2009), pp. 60-66. [10.4028/www.scientific.net/SSP.151.60]

Hybrid glass mat reinforced polypropylene-montmorillonite nanocomposites

Dalle Vacche, Sara;
2009

Abstract

Although addition of montmorillonite (MMT) clay to isotactic polypropylene (iPP) results in large increases in the melt viscosity at low shear rates, satisfactory impregnation of glass mats is obtained with iPP/MMT under conditions typical of industrial processing, and the MMT is well dispersed throughout the resulting composites. However, the MMT is also shown to retard relaxation of the glass mat, leading to non-uniform through-thickness glass fiber distributions. Thus, depending on the initial lay-up and hence on the initial surface fiber concentration, the bending modulus of the consolidated specimens may either increase or decrease with increasing matrix MMT content, whereas the tensile modulus remains consistent with the predictions of micromechanical models based on the assumption of a uniform glass fiber distribution. The presence of matrix-rich layers at surfaces of specimens containing MMT is also shown to promote crack initiation and induce premature failure in flexural tests.
File in questo prodotto:
File Dimensione Formato  
Plummer 2009 - Solid state phenom.pdf

accesso riservato

Descrizione: Articolo principale
Tipologia: 2a Post-print versione editoriale / Version of Record
Licenza: Non Pubblico - Accesso privato/ristretto
Dimensione 4.79 MB
Formato Adobe PDF
4.79 MB Adobe PDF   Visualizza/Apri   Richiedi una copia
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11583/2912181