In this paper, the impact of the post-heat-treatment on the structural and spectroscopic properties as well as on the chemical durability of a thermally stable Er3+-doped phosphate glass in the system P2O5 - K2O - Al2O3 - B2O3 - BaO - PbO - La2O3 - Gd2O3 is reported. Two crystalline phases, namely La, Gd-monazite and AlKP2O7, were found to precipitate from the surface of the glass after heat-treatment, as confirmed by both X-ray Diffraction (XRD) and Scanning Electron Microscopy/Energy Dispersive X-ray (SEM/EDX) analyses. Moreover, the heat-treatment was responsible for the formation of a more polymerized glass network close to the surface crystalline layer as evidenced using micro-Raman spectroscopy. From the changes in the Er3+ optical properties, some of the Er3+ ions are suspected to enter in the crystals. Both the as-prepared and heat-treated glasses were subjected to a degradation test in hydrochloric acid (HCl) and showed a congruent and incongruent dissolution behavior, respectively.

Effect of post-heat-treatment on the structural, spectroscopic and dissolution properties of a highly stable Er3+-doped multi-component phosphate glass / Pugliese, Diego; Veber, Alexander; Lemière, Arnaud; Boetti, Nadia G.; Petit, Laeticia. - In: JOURNAL OF ALLOYS AND COMPOUNDS. - ISSN 0925-8388. - ELETTRONICO. - 883:(2021), p. 160878. [10.1016/j.jallcom.2021.160878]

Effect of post-heat-treatment on the structural, spectroscopic and dissolution properties of a highly stable Er3+-doped multi-component phosphate glass

Pugliese, Diego;Boetti, Nadia G.;
2021

Abstract

In this paper, the impact of the post-heat-treatment on the structural and spectroscopic properties as well as on the chemical durability of a thermally stable Er3+-doped phosphate glass in the system P2O5 - K2O - Al2O3 - B2O3 - BaO - PbO - La2O3 - Gd2O3 is reported. Two crystalline phases, namely La, Gd-monazite and AlKP2O7, were found to precipitate from the surface of the glass after heat-treatment, as confirmed by both X-ray Diffraction (XRD) and Scanning Electron Microscopy/Energy Dispersive X-ray (SEM/EDX) analyses. Moreover, the heat-treatment was responsible for the formation of a more polymerized glass network close to the surface crystalline layer as evidenced using micro-Raman spectroscopy. From the changes in the Er3+ optical properties, some of the Er3+ ions are suspected to enter in the crystals. Both the as-prepared and heat-treated glasses were subjected to a degradation test in hydrochloric acid (HCl) and showed a congruent and incongruent dissolution behavior, respectively.
File in questo prodotto:
File Dimensione Formato  
Pre-print autore.pdf

accesso aperto

Descrizione: Pre-print autore
Tipologia: 1. Preprint / submitted version [pre- review]
Licenza: PUBBLICO - Tutti i diritti riservati
Dimensione 1.32 MB
Formato Adobe PDF
1.32 MB Adobe PDF Visualizza/Apri
Post-print autore.pdf

Open Access dal 20/06/2023

Descrizione: Post-print autore
Tipologia: 2. Post-print / Author's Accepted Manuscript
Licenza: Creative commons
Dimensione 1.25 MB
Formato Adobe PDF
1.25 MB Adobe PDF Visualizza/Apri
Post-print editore.pdf

non disponibili

Descrizione: Post-print editoriale
Tipologia: 2a Post-print versione editoriale / Version of Record
Licenza: Non Pubblico - Accesso privato/ristretto
Dimensione 5.74 MB
Formato Adobe PDF
5.74 MB Adobe PDF   Visualizza/Apri   Richiedi una copia
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11583/2909832