The production of magnesium alloy WE43 was achieved by selective laser melting (SLM). The alloy was investigated after SLM, hot isostatic pressing (HIP), and solutionising heat treatment. The microstructure and corrosion behaviour of the specimens were carefully characterised, whilst assessed and contrast relative to the conventionally cast alloy counterpart. The SLM prepared specimens possess a unique microstructure comprising fine grains growing with a strong [0001] texture along the building direction with a low fraction of process-induced and metallurgical defects, reaching < 0.1 %, after optimising the SLM parameters and the HIP treatment. Electrochemical measurements demonstrated that the SLM prepared WE43 is cathodically more active as compared with its cast counterpart. It is proposed that this behaviour is due to a high density of zirconium-rich oxide particles uniformly distributed throughout the alloy microstructure as well as the alterations in the chemical composition of the solid-solution matrix originating from the high cooling rates of SLM. It was also noted that the oxide particles are mainly sourced by powder. The present results suggest that the corrosion of SLM prepared Mg alloys could be greatly improved once the influence of powder characteristics is further understood and controlled.

A detailed microstructural and corrosion analysis of magnesium alloy WE43 manufactured by selective laser melting / Esmaily, M.; Zeng, Z.; Mortazavi, A. N.; Gullino, A.; Choudhary, S.; Derra, T.; Benn, F.; D'Elia, F.; Muther, M.; Thomas, S.; Huang, A.; Allanore, A.; Kopp, A.; Birbilis, N.. - In: ADDITIVE MANUFACTURING. - ISSN 2214-8604. - 35:(2020), pp. 1-17. [10.1016/j.addma.2020.101321]

A detailed microstructural and corrosion analysis of magnesium alloy WE43 manufactured by selective laser melting

Gullino A.;
2020

Abstract

The production of magnesium alloy WE43 was achieved by selective laser melting (SLM). The alloy was investigated after SLM, hot isostatic pressing (HIP), and solutionising heat treatment. The microstructure and corrosion behaviour of the specimens were carefully characterised, whilst assessed and contrast relative to the conventionally cast alloy counterpart. The SLM prepared specimens possess a unique microstructure comprising fine grains growing with a strong [0001] texture along the building direction with a low fraction of process-induced and metallurgical defects, reaching < 0.1 %, after optimising the SLM parameters and the HIP treatment. Electrochemical measurements demonstrated that the SLM prepared WE43 is cathodically more active as compared with its cast counterpart. It is proposed that this behaviour is due to a high density of zirconium-rich oxide particles uniformly distributed throughout the alloy microstructure as well as the alterations in the chemical composition of the solid-solution matrix originating from the high cooling rates of SLM. It was also noted that the oxide particles are mainly sourced by powder. The present results suggest that the corrosion of SLM prepared Mg alloys could be greatly improved once the influence of powder characteristics is further understood and controlled.
File in questo prodotto:
File Dimensione Formato  
1-s2.0-S221486042030693X-main.pdf

non disponibili

Tipologia: 2a Post-print versione editoriale / Version of Record
Licenza: Non Pubblico - Accesso privato/ristretto
Dimensione 8.13 MB
Formato Adobe PDF
8.13 MB Adobe PDF   Visualizza/Apri   Richiedi una copia
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11583/2840181