Stereolithography (SL) stands out as a relatively fast additive manufacturing method to produce thermoset components with high resolutions. The majority of SL resins consist of acrylate monomers which result in materials with cur-ing-induced shrinkage problems and this, in addition to the incomplete and non-uniform conversions reached in the SL process, results in poor mechanical properties. To address this issue, a dual-curing formulation was developed by mixing an epoxy monomer into a commercial multi-acrylate SL resin: the first curing stage is acrylate free-radical photopolymerization at ambient temperature, and the second curing stage is cationic epoxy homopolymerization at higher temperatures. The fully dual-cured materials are macroscopically homogeneous, with nanoscale domains observed by Atomic Force Mi-croscopy (AFM), and with unimodal tan delta peaks observed in Dynamic Mechanical Analysis (DMA). The uncured material was storage stable at ambient conditions for at least 9 weeks since the epoxy part was virtually unreactive at these temper-atures. With the dual-cured materials, a nearly 10-fold increase in Young’s modulus was achieved over the neat acrylate resin. At the thermal curing stage, the presence of diperoxyketal thermal radical initiator to the liquid formulation facilitated the polymerization of unreacted acrylates that remained from the SL process simultaneously with epoxy homopolymerization and helped the material attain improved properties.

Dual-curable stereolithography resins for superior thermomechanical properties / Konuray, O.; Di Donato, F.; Sangermano, M.; Bonada, J.; Tercjak, A.; Fernandez-Francos, X.; Serra, A.; Ramis, X.. - In: EXPRESS POLYMER LETTERS. - ISSN 1788-618X. - ELETTRONICO. - 14:9(2020), pp. 881-894. [10.3144/expresspolymlett.2020.72]

Dual-curable stereolithography resins for superior thermomechanical properties

Sangermano M.;
2020

Abstract

Stereolithography (SL) stands out as a relatively fast additive manufacturing method to produce thermoset components with high resolutions. The majority of SL resins consist of acrylate monomers which result in materials with cur-ing-induced shrinkage problems and this, in addition to the incomplete and non-uniform conversions reached in the SL process, results in poor mechanical properties. To address this issue, a dual-curing formulation was developed by mixing an epoxy monomer into a commercial multi-acrylate SL resin: the first curing stage is acrylate free-radical photopolymerization at ambient temperature, and the second curing stage is cationic epoxy homopolymerization at higher temperatures. The fully dual-cured materials are macroscopically homogeneous, with nanoscale domains observed by Atomic Force Mi-croscopy (AFM), and with unimodal tan delta peaks observed in Dynamic Mechanical Analysis (DMA). The uncured material was storage stable at ambient conditions for at least 9 weeks since the epoxy part was virtually unreactive at these temper-atures. With the dual-cured materials, a nearly 10-fold increase in Young’s modulus was achieved over the neat acrylate resin. At the thermal curing stage, the presence of diperoxyketal thermal radical initiator to the liquid formulation facilitated the polymerization of unreacted acrylates that remained from the SL process simultaneously with epoxy homopolymerization and helped the material attain improved properties.
File in questo prodotto:
File Dimensione Formato  
dual-cure Stereolithography.pdf

accesso aperto

Tipologia: 2a Post-print versione editoriale / Version of Record
Licenza: PUBBLICO - Tutti i diritti riservati
Dimensione 734.49 kB
Formato Adobe PDF
734.49 kB Adobe PDF Visualizza/Apri
Pubblicazioni consigliate

Caricamento pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: http://hdl.handle.net/11583/2839249