Archivio Istituzionale della RicercaNanocrystalline praseodymium doped zirconia powders were produced using a microwave driven hydrothermal process under pressures up to 8 GPa. The aim of the work was to evaluate the effect of synthesis conditions on the phase composition and grain size of nanopowders of zirconia with Pr in solid solutions having Pr contents of: 0, 0.5, 1, 5 and 10 mol %.
Microwave-hydrothermal synthesis of nanocrystalline Pr-doped zirconia powders at pressures up to 8 MPa / Bondioli, Federica; A., Ferrari; S., Braccini; C., Leonelli; G., Pellacani; A., Opalinska; T., Chudoba; E., Grzanka; B., Palosz; W., Lojkowski. - In: DIFFUSION AND DEFECT DATA, SOLID STATE DATA. PART B, SOLID STATE PHENOMENA. - ISSN 1012-0394. - 94:(2003), pp. 193-196.
Microwave-hydrothermal synthesis of nanocrystalline Pr-doped zirconia powders at pressures up to 8 MPa
BONDIOLI, Federica;
2003
Abstract
Nanocrystalline praseodymium doped zirconia powders were produced using a microwave driven hydrothermal process under pressures up to 8 GPa. The aim of the work was to evaluate the effect of synthesis conditions on the phase composition and grain size of nanopowders of zirconia with Pr in solid solutions having Pr contents of: 0, 0.5, 1, 5 and 10 mol %.
Pubblicazioni consigliate
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.
https://hdl.handle.net/11583/2725396
Attenzione
Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo