The aim of this study was the surface functionalization of a new green ceramic material, obtained using packaging glass waste (PGW), to improve its gleanability. This objective was reached through the deposition by air-brushing of a nanostructured coating based on titania–silica sol–gel suspension. The coatings were deposited on both glazed and unglazed ceramic substrates and the thermal treatment conditions (temperature) were optimized. The obtained results suggest that the applied coatings are transparent and show a good scratch resistance and photocatalytic activity under the tested conditions. The photo degradation process and the mechanical properties are clearly affected by the thermal treatment and thus by the sample surface roughness. The best surface properties were obtained with a thermal treatment at temperature of 150°C. These coatings do not exhibit either cracks from the substrate. All in all, the developed surface modified ceramic material is attractive as potential sustainable building material.

Surface properties of new green building material after TiO2–SiO2 coatings deposition / Taurino, Rosa; Barbieri, Luisa; Bondioli, Federica. - In: CERAMICS INTERNATIONAL. - ISSN 0272-8842. - 42:4(2016), pp. 4866-4874. [10.1016/j.ceramint.2015.12.002]

Surface properties of new green building material after TiO2–SiO2 coatings deposition

Bondioli Federica
2016

Abstract

The aim of this study was the surface functionalization of a new green ceramic material, obtained using packaging glass waste (PGW), to improve its gleanability. This objective was reached through the deposition by air-brushing of a nanostructured coating based on titania–silica sol–gel suspension. The coatings were deposited on both glazed and unglazed ceramic substrates and the thermal treatment conditions (temperature) were optimized. The obtained results suggest that the applied coatings are transparent and show a good scratch resistance and photocatalytic activity under the tested conditions. The photo degradation process and the mechanical properties are clearly affected by the thermal treatment and thus by the sample surface roughness. The best surface properties were obtained with a thermal treatment at temperature of 150°C. These coatings do not exhibit either cracks from the substrate. All in all, the developed surface modified ceramic material is attractive as potential sustainable building material.
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11583/2723292
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo