Crystalline BaFe12O19 powder was synthetized by auto-combustion sol gel method, in which citric acid was used both as a fuel and chelating agent. The pre-combusted precursor was calcined at 900 °C for 1 h and characterized by laser granulometry, X-ray diffraction, scanning electron microscopy, thermal analysis and transmission electron microscopy. Sensors were prepared by screen-printing the sensing material onto α-alumina substrates with platinum interdigitated electrodes. After drying overnight, sensors were fired at 600 °C in air. The sensor response was measured in the range 150 °C–350 °C performing all measurements in a flow chamber at a constant flow rate of 1 L/min of dry air in the range 200–500 ppb O3. Response time and recovery time (e.g., the times taken for the sensor to attain 90% of total impedance change from its initial impedance value) were determined, together with cross-sensitivity tests towards NH3, CH4, humidity, CO2, N2O and NO2. Sensor's maximum responses were observed at 250 °C, with SR equal to 18% under 500 ppb O3, and SR of 10% under 200 ppb O3. Such results are extremely encouraging and support the exploitation of barium hexaferrite as relatively low-temperature ozone sensors.
Barium hexaferrite thick-films for ozone detection at low temperature / Ziegler, Daniele; Marchisio, Andrea; Montanaro, Laura; Palmero, Paola; Tulliani, Jean Marc Christian. - In: SOLID STATE IONICS. - ISSN 0167-2738. - ELETTRONICO. - 320(2018), pp. 24-32. [10.1016/j.ssi.2018.02.028]
Titolo: | Barium hexaferrite thick-films for ozone detection at low temperature | |
Autori: | ||
Data di pubblicazione: | 2018 | |
Rivista: | ||
Digital Object Identifier (DOI): | http://dx.doi.org/10.1016/j.ssi.2018.02.028 | |
Appare nelle tipologie: | 1.1 Articolo in rivista |
File in questo prodotto:
File | Descrizione | Tipologia | Licenza | |
---|---|---|---|---|
Barium hexaferrite thick-films for ozone detection at low temperature.pdf | Barium hexaferrite thick-films for ozone detection at low temperature | 2a Post-print versione editoriale / Version of Record | Non Pubblico - Accesso privato/ristretto | Administrator Richiedi una copia |
http://hdl.handle.net/11583/2701332