In the recent years the interest of the research community towards multiferroic composite materials was growing fast [1,2]. A number of papers relates to bulk materials while less attention is focused on films. Electrophoretic deposition (EPD) was applied to prepare magnetoelectric (ME) composite bilayer thick films based on piezoelectric phases and cobalt ferrite. The deposition/co-depositionwere made from colloidal suspensions in ethanolkeeping constant voltage and recording the current. Good adhesion and compaction of the green film were achieved by optimization of deposition voltage and time while high density of the film and minimized interphase reactions occurred after sintering. The chemical activity between the two layers was controlled through the batches composition and it could lead to the synthesis of complex engineered structures.The deposited volume, the mixing of dielectric and magnetic phases and the density and ordering of the films have been verified by electron scanning microscopy after heat treatment. The piezoelectric properties were measured on the sintered films. [1] N.A. Spaldin, M. Fiebig, Science 309 (2005) 391. [2] R. Ramesh, N.A. Spaldin, Nat. Mater. 6 (2007) 21.

Magnetoelectric composite bilayer films by electrophoretic deposition / Galizia, Pietro; Gardini, Davide; Ciuchi, Ioana Veronica; Galassi, Carmen. - ELETTRONICO. - (2015). (Intervento presentato al convegno 14th International Conference of the European Ceramic Society tenutosi a Toledo (Spagna) nel 21-25 June, 2015).

Magnetoelectric composite bilayer films by electrophoretic deposition

GALIZIA, PIETRO;
2015

Abstract

In the recent years the interest of the research community towards multiferroic composite materials was growing fast [1,2]. A number of papers relates to bulk materials while less attention is focused on films. Electrophoretic deposition (EPD) was applied to prepare magnetoelectric (ME) composite bilayer thick films based on piezoelectric phases and cobalt ferrite. The deposition/co-depositionwere made from colloidal suspensions in ethanolkeeping constant voltage and recording the current. Good adhesion and compaction of the green film were achieved by optimization of deposition voltage and time while high density of the film and minimized interphase reactions occurred after sintering. The chemical activity between the two layers was controlled through the batches composition and it could lead to the synthesis of complex engineered structures.The deposited volume, the mixing of dielectric and magnetic phases and the density and ordering of the films have been verified by electron scanning microscopy after heat treatment. The piezoelectric properties were measured on the sintered films. [1] N.A. Spaldin, M. Fiebig, Science 309 (2005) 391. [2] R. Ramesh, N.A. Spaldin, Nat. Mater. 6 (2007) 21.
2015
9788460692577
File in questo prodotto:
File Dimensione Formato  
2015-06-ECerS2015-Toledo-Presentation.pdf

accesso aperto

Descrizione: Presented Slides at the 14th International Conference of the European Ceramic Society
Tipologia: Altro materiale allegato
Licenza: PUBBLICO - Tutti i diritti riservati
Dimensione 2.34 MB
Formato Adobe PDF
2.34 MB Adobe PDF Visualizza/Apri
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11583/2646489
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo