IRIS è la soluzione IT che facilita la raccolta e la gestione dei dati relativi alle attività e ai prodotti della ricerca. Fornisce a ricercatori, amministratori e valutatori gli strumenti per monitorare i risultati della ricerca, aumentarne la visibilità e allocare in modo efficace le risorse disponibili.
EnglishThis work describes the performance and testing of a glass-ceramic sealant used to join the ceramic electrolyte (anode-supported-electrolyte (ASE)) to the metallic interconnect (Crofer22APU) in planar SOFC stacks. The designed glass-ceramic sealant is a barium and boron free silica-based glass, which crystallizes by means of the heat-treatment after being deposited on substrates by the slurry technique. Joined ASE/glass-ceramic seal/Crofer22APU samples were tested for 500 h in H2–3H2O atmosphere at the fuel cell operating temperature of 800 ◦C. Moreover, the joined ASE/glass-ceramic seal/Crofer22APU samples were submitted to three thermal cycles each of 120 h duration, in order to evaluate the thermomechanical stability of the sealant. The microstructures and elemental distribution at Crofer22APU/glass-ceramic and ASE/glass-ceramic interfaces were investigated. SEM micrograph observations of joined samples that underwent cyclic thermal tests and exposure for 500 h in H2–3H2O atmosphere showed that the adhesion between the glass-ceramic and Crofer22APU at either interface was very good and no microstructural changes were detected at the interfacial boundaries. The study showed that the use of the glass-ceramic was successful in preventing strong adverse corrosion effects at the Crofer22APU/glass-ceramic sealant interface.
Performance and testing of glass-ceramic sealant used to join anode-supported-electrolyte to Crofer22APU in planar solid oxide fuel cells / SMEACETTO F.; CHRYSANTHOU A; SALVO M; ZHANG Z; FERRARIS M. - In: JOURNAL OF POWER SOURCES. - ISSN 0378-7753. - STAMPA. - 190:2(2009), pp. 402-407. [10.1016/j.jpowsour.2009.01.042]
| Titolo: | Performance and testing of glass-ceramic sealant used to join anode-supported-electrolyte to Crofer22APU in planar solid oxide fuel cells | |
| Autori: | ||
| Data di pubblicazione: | 2009 | |
| Rivista: | ||
| Digital Object Identifier (DOI): | http://dx.doi.org/10.1016/j.jpowsour.2009.01.042 | |
| Appare nelle tipologie: | 1.1 Articolo in rivista |
File in questo prodotto:
| File | Descrizione | Tipologia | Licenza | |
|---|---|---|---|---|
| 1897637.pdf | 2. Post-print / Author's Accepted Manuscript | Non Pubblico - Accesso privato/ristretto | Administrator Richiedi una copia |
http://hdl.handle.net/11583/1897637
Copyright © 2022