The corrosion performance of two crystalline Co–Ni–Pr and Co–Ni–Er alloys (Pr5.5Co58Ni36.5 and Er6.5Co57.5Ni36) in an alkaline solution, like the one used in water electrolysis, was studied and compared with that of a commercially employed binary Co–Ni alloy (Co57Ni43) in order to assess the influence of rare earth elements on its corrosion behaviour. Light electron microscopy, scanning electron microscopy and quantitative electron probe microanalysis were used to characterize the samples prior to the electro- chemical tests. The experiments were carried out in 1 M KOH solution at 298 K. Potentiodynamic polar- ization curves and potentiostatic current decay transients revealed that Co–Ni–R alloys significantly improved resistance to corrosion compared with Co–Ni alloys, in spite of their two-phase microstructure, as a direct consequence of the presence of the praseodymium and erbium rare earth metals in the anodic layer formation.
Effect of rare earth metals addition on the corrosion behaviour of crystalline Co-Ni alloys in alkaline solution / ROSALBINO F.; DELSANTE S; BORZONE G; ANGELINI E. - In: JOURNAL OF ELECTROANALYTICAL CHEMISTRY. - ISSN 1572-6657. - ELETTRONICO. - 622(2008), pp. 161-164. [10.1016/j.jelechem.2008.05.015]
|Titolo:||Effect of rare earth metals addition on the corrosion behaviour of crystalline Co-Ni alloys in alkaline solution|
|Data di pubblicazione:||2008|
|Digital Object Identifier (DOI):||http://dx.doi.org/10.1016/j.jelechem.2008.05.015|
|Appare nelle tipologie:||1.1 Articolo in rivista|