Cement composites were realized containing graphene-based materials having different oxygen content (from 0 to 45%). It was found that the polarity of the reinforcement influences both the dispersion in water and the chemical interaction with the hydrated cement matrix, and thus the mechanical performance of the composites. In particular, the reinforcements with the highest oxygen content result aggregated while the cement with the highest strength is obtained with functionalized graphene, containing 5% oxygen, where the surface has sufficient polar groups to guarantee proper dispersion and interaction with the hydrated cement.

Relationship between oxygen content of graphene and mechanical properties of cement-based composites / Lavagna, L.; Massella, D.; Priola, E.; Pavese, M.. - In: CEMENT & CONCRETE COMPOSITES. - ISSN 0958-9465. - ELETTRONICO. - 115:(2021), p. 103851. [10.1016/j.cemconcomp.2020.103851]

Relationship between oxygen content of graphene and mechanical properties of cement-based composites

Lavagna L.;Massella D.;Pavese M.
2021

Abstract

Cement composites were realized containing graphene-based materials having different oxygen content (from 0 to 45%). It was found that the polarity of the reinforcement influences both the dispersion in water and the chemical interaction with the hydrated cement matrix, and thus the mechanical performance of the composites. In particular, the reinforcements with the highest oxygen content result aggregated while the cement with the highest strength is obtained with functionalized graphene, containing 5% oxygen, where the surface has sufficient polar groups to guarantee proper dispersion and interaction with the hydrated cement.
File in questo prodotto:
File Dimensione Formato  
ccc graphene.pdf

Open Access dal 24/10/2022

Tipologia: 2. Post-print / Author's Accepted Manuscript
Licenza: Creative commons
Dimensione 2.77 MB
Formato Adobe PDF
2.77 MB Adobe PDF Visualizza/Apri
cemento grafene.pdf

non disponibili

Tipologia: 2a Post-print versione editoriale / Version of Record
Licenza: Non Pubblico - Accesso privato/ristretto
Dimensione 3.13 MB
Formato Adobe PDF
3.13 MB Adobe PDF   Visualizza/Apri   Richiedi una copia
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11583/2854325