Lithium Metal Batteries (LMB) require solid or quasi-solid electrolytes able to block dendrites formation during cell cycling. Polymer-in-ceramic nanocomposites with the ceramic fraction exceeding the one normally used as the filler (>10 ÷ 15 wt%) are among the most interesting options on the table. Here, we report on a new hybrid material encompassing brush-like TiO2 nanocrystals functionalized with low molecular weight poly(ethylene oxide) (PEO). The nanocomposite electrolyte membranes are then obtained by blending the brush-like nanocrystals with high molecular weight PEO and LiTFSI. The intrinsic chemical compatibility among the PEO moieties allows a TiO2 content as high as ∼39 wt% (90:10 w/w functionalized nanocrystals/PEOLiTFSI), while maintaining good processability and mechanical resistance. The 50:50 w/w nanocomposite electrolyte (18.8 wt% functionalized TiO2) displays ionic conductivity of 3 × 10−4 S cm−1 at 70 °C. Stripping/plating experiments show an excellent long-term behavior even at relatively high currents of 200 μA cm−2 . Upon testing in a lab-scale Li/electrolyte/LiFePO4 cell, the material delivers 130 mAh g−1 and 120 mAh g−1 after 40 and 50 cycles at 0.05 and 0.1 mA, respectively, with Coulombic efficiency exceeding 99.5%, which demonstrates the very promising prospects of these newly developed nanocomposite solid electrolyte for future development of LMBs.

Polymer-in-Ceramic Nanocomposite Solid Electrolyte for Lithium Metal Batteries Encompassing PEO-Grafted TiO2 Nanocrystals / Colombo, Francesco; Bonizzoni, Simone; Ferrara, Chiara; Simonutti, Roberto; Mauri, Michele; Falco, Marisa; Gerbaldi, Claudio; Mustarelli, Piercarlo; Ruffo, Riccardo. - In: JOURNAL OF THE ELECTROCHEMICAL SOCIETY. - ISSN 1945-7111. - ELETTRONICO. - 167:(2020), pp. 070535-1-070535-6. [10.1149/1945-7111/ab7c72]

Polymer-in-Ceramic Nanocomposite Solid Electrolyte for Lithium Metal Batteries Encompassing PEO-Grafted TiO2 Nanocrystals

Marisa Falco;Claudio Gerbaldi;
2020

Abstract

Lithium Metal Batteries (LMB) require solid or quasi-solid electrolytes able to block dendrites formation during cell cycling. Polymer-in-ceramic nanocomposites with the ceramic fraction exceeding the one normally used as the filler (>10 ÷ 15 wt%) are among the most interesting options on the table. Here, we report on a new hybrid material encompassing brush-like TiO2 nanocrystals functionalized with low molecular weight poly(ethylene oxide) (PEO). The nanocomposite electrolyte membranes are then obtained by blending the brush-like nanocrystals with high molecular weight PEO and LiTFSI. The intrinsic chemical compatibility among the PEO moieties allows a TiO2 content as high as ∼39 wt% (90:10 w/w functionalized nanocrystals/PEOLiTFSI), while maintaining good processability and mechanical resistance. The 50:50 w/w nanocomposite electrolyte (18.8 wt% functionalized TiO2) displays ionic conductivity of 3 × 10−4 S cm−1 at 70 °C. Stripping/plating experiments show an excellent long-term behavior even at relatively high currents of 200 μA cm−2 . Upon testing in a lab-scale Li/electrolyte/LiFePO4 cell, the material delivers 130 mAh g−1 and 120 mAh g−1 after 40 and 50 cycles at 0.05 and 0.1 mA, respectively, with Coulombic efficiency exceeding 99.5%, which demonstrates the very promising prospects of these newly developed nanocomposite solid electrolyte for future development of LMBs.
File in questo prodotto:
File Dimensione Formato  
F. Colombo et al., J. Electrochem. Soc. 167 (2020) 070535.pdf

accesso aperto

Descrizione: Versione OPEN ACCESS, scaricabile online
Tipologia: 2a Post-print versione editoriale / Version of Record
Licenza: Creative commons
Dimensione 1.03 MB
Formato Adobe PDF
1.03 MB Adobe PDF Visualizza/Apri
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11583/2818643