Synthesis optimization of carbon-supported ZrO2 nanoparticles from different organometallic precursors

We report here the synthesis of carbon-supported ZrO2 nanoparticles from zirconium oxyphthalocyanine (ZrOPc) and acetylacetonate [Zr(acac)4]. Using thermogravimetric analysis (TGA) coupled with mass spectrometry (MS), we could investigate the thermal decomposition behavior of the chosen precursors. According to those results, we chose the heat treatment temperatures (THT) using partial oxidizing (PO) and reducing (RED) atmosphere. By X-ray diffraction we detected structure and size of the nanoparticles; the size was further confirmed by transmission electron microscopy. ZrO2 formation happens at lower temperature with Zr(acac)4 than with ZrOPc, due to the lower thermal stability and a higher oxygen amount in Zr(acac)4. Using ZrOPc at THT C900 °C, PO conditions facilitate the crystallite growth and formation of distinct tetragonal ZrO2, while with Zr(acac)4 a distinct tetragonal ZrO2 phase is observed already at THT C750 °C in both RED and PO conditions. Tuning of ZrO2 nanocrystallite size from 5 to 9 nm by varying the precursor loading is also demonstrated. The chemical state of zirconium was analyzed by X-ray photoelectron spectroscopy, which confirms ZrO2 formation from different synthesis routes.