The main aim of the paper are analysis the effect of the processing conditions on the magnetic behaviour of iron insulated powder compound (IIPC) materials admixed by aluminium alloy at low frequencies. Results show that the higher applied compactive pressures cause a greater reduction of volumes and of present porosities. The behaviour of powders during the pressing process and heat treatment is important question in the improving of IIPC materials to give a suitable combination between pressing pressure, sintering temperature and time as well as magnetic properties. The coercivity and the remanence increased with increasing applied pressure that is also attributed to the enhanced densification and promote porosity reduction. However, the subsequent decrease of remanence and increase of coercivity are observed in terms of addition of aluminium alloys.

The role of processing conditions on the magnetic properties of insulated iron powder compounds at low frequencies / Bidulsky, Robert; ACTIS GRANDE, Marco; Bidulska, J.; Forno, Ilaria. - In: JOURNAL OF OPTOELECTRONICS AND ADVANCED MATERIALS. - ISSN 1454-4164. - STAMPA. - 14, N°11-12:(2012), pp. 946-951.

The role of processing conditions on the magnetic properties of insulated iron powder compounds at low frequencies

BIDULSKY, ROBERT;ACTIS GRANDE, MARCO;FORNO, ILARIA
2012

Abstract

The main aim of the paper are analysis the effect of the processing conditions on the magnetic behaviour of iron insulated powder compound (IIPC) materials admixed by aluminium alloy at low frequencies. Results show that the higher applied compactive pressures cause a greater reduction of volumes and of present porosities. The behaviour of powders during the pressing process and heat treatment is important question in the improving of IIPC materials to give a suitable combination between pressing pressure, sintering temperature and time as well as magnetic properties. The coercivity and the remanence increased with increasing applied pressure that is also attributed to the enhanced densification and promote porosity reduction. However, the subsequent decrease of remanence and increase of coercivity are observed in terms of addition of aluminium alloys.
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11583/2505107
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo